新型巯基功能化二氧化硅微球的制备及其对银离子的吸附

刘岩; 白晓; 李婷婷; 孙杨; 沈启慧; 于东冬; 周建光

您当前的位置：

首页 >

文章列表页 >

新型巯基功能化二氧化硅微球的制备及其对银离子的吸附

研究论文 | 更新时间：2023-12-11

- 新型巯基功能化二氧化硅微球的制备及其对银离子的吸附
- Facile preparation of thiol-functionalized SiO₂ microspheres and their adsorption to silver ions
- 中山大学学报(自然科学版)(中英文) 2016年55卷第6期页码：136-139
- 作者机构：
  
  1. 吉林化工学院化学与制药工程学院,吉林,吉林,132022
  2. 
  3. 浙江大学医院,浙江,杭州,310027
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2016，
  
  网络出版日期：2016-11-25，
扫描看全文
刘岩, 白晓, 李婷婷, 等. 新型巯基功能化二氧化硅微球的制备及其对银离子的吸附[J]. 中山大学学报(自然科学版)(中英文), 2016,55(6):136-139.

LIU Yan, BAI Xiao, LI Tingting, et al. Facile preparation of thiol-functionalized SiO₂ microspheres and their adsorption to silver ions[J]. Acta Scientiarum Naturalium Universitatis SunYatseni, 2016,55(6):136-139.
刘岩, 白晓, 李婷婷, 等. 新型巯基功能化二氧化硅微球的制备及其对银离子的吸附[J]. 中山大学学报(自然科学版)(中英文), 2016,55(6):136-139. DOI：

LIU Yan, BAI Xiao, LI Tingting, et al. Facile preparation of thiol-functionalized SiO₂ microspheres and their adsorption to silver ions[J]. Acta Scientiarum Naturalium Universitatis SunYatseni, 2016,55(6):136-139. DOI：

摘要

表面具有大量巯基的二氧化硅微球与介孔二氧化硅一样，具有吸附重金属离子的功能。通过溶胶凝胶一步法制备巯基功能化的二氧化硅微球，该微球粒度分布均匀、成球率高，直径在1 μm左右。红外和拉曼光谱证明，微球表面富含大量的巯基，超短的吸附平衡时间说明巯基与Ag

迅速螯合，而不同于介孔的扩散吸附。溶液的pH对Ag

吸附量的影响不明显，巯基功能化的微球对Ag

的吸附遵守Slips等温模型，最大吸附量能够达到102 mg/g，并且拟合度达到99.6%。

Abstract

The SiO

microspheres with abundant thiol on the surface have the same property of adsorption to heavy metal ions as that of the mesoporous silica. In onepot

the thiol-functionalized SiO

microspheres were prepared by a sol-gel method

and SiO

microspheres had a narrow particle size distribution and well sphere with diameter around 1 μm. FTIR and Raman spectroscopy confirmed there were a great amount of thiols on the surface of microspheres. Meanwhile

the adsorption process of silver ions by the microspheres finished within u1tra-short time

which was in accord with the chelation of silver ions and thiols. And that was different from the diffusion adsorption of mesoporous silica. Furthermore

the pH value of solution had little effect on the adsorption capacity of silver ions and the adsorption maximum is 102 mg/g in Slips isotherm with R

=99.6%.

关键词

巯基二氧化硅微球吸附银离子

Keywords

thiolSiO2microspheresadsorptionsilver ions

references

浏览量

230

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

核壳结构柠檬酸改性纳米磁性颗粒的特性研究

甘蔗渣吸附剂的制备及其对Pb²⁺、Cu^2+、Cr³⁺的吸附动力学研究

羟基磷灰石的粒径及其掺入牙膏后对镉离子吸附作用的研究

不同粒径纳米羟基磷灰石牙膏对铅离子的吸附研究

双重磁响应复合微球的制备及吸附性能研究