Stress Corrosion of Concrete Exposed to Immersion-dry and Loading Conditions

ZHANG Liming; YU Hongfa; NING Zuojun

您当前的位置：

首页 >

文章列表页 >

Stress Corrosion of Concrete Exposed to Immersion-dry and Loading Conditions

更新时间：2023-12-11

- Stress Corrosion of Concrete Exposed to Immersion-dry and Loading Conditions
- Acta Scientiarum Naturalium Universitatis SunYatseni Vol. 52, Issue 3, Pages: 40-44(2013)
- 作者机构：
  
  1. 南京航空航天大学土木工程系,江苏,南京,210016
  2. 
  3. 吉林交通职业技术学院,吉林,长春,130012
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2013，
  
  Published Online：25 May 2013，
扫描看全文
ZHANG Liming, YU Hongfa, NING Zuojun. Stress Corrosion of Concrete Exposed to Immersion-dry and Loading Conditions. [J]. Acta Scientiarum Naturalium Universitatis SunYatseni 52(3):40-44(2013)
DOI：

ZHANG Liming, YU Hongfa, NING Zuojun. Stress Corrosion of Concrete Exposed to Immersion-dry and Loading Conditions. [J]. Acta Scientiarum Naturalium Universitatis SunYatseni 52(3):40-44(2013) DOI：

摘要

研究了水灰比分别为053、035和027的普通混凝土(OPC)、高性能混凝土( HPC) 和高强混凝土( HSC)在盐湖卤水浸烘、浸烘+30%荷载和盐湖现场暴露环境下盐应力腐蚀行为。试验结果表明：在不同环境作用下

混凝土在应力腐蚀作用下的相对动弹性模量要经历强化和劣化2个发展阶段

强化和劣化阶段的时间与试验环境和混凝土类型密切相关。水灰比越大，劣化速率越大强化时间越短。浸烘循环+30%荷载作用显著加速了混凝土应力腐蚀破坏进程。OPC应力腐蚀的强化段在浸烘循环+30%荷载时间与长度暴露环境条件的相应时间长度分别压缩了67%。在浸烘+30%荷载循环作用下

在强化阶段HSC发生应力腐蚀的干湿循环次数分别比OPC和HPC延长了18倍

因此，在中国盐湖地区，HSC表现出更强的抗应力腐蚀能力。

Abstract

The considered concretes include ordinary portland cement (OPC)、High Strength Concrete( HSC) and High performance Concrete ( HPC)with the water to binder 0.53、0.35 and 0.27 under three different conditions. This study revealed that the relative dynamic elastic modulus of concrete went through strengthen and deterioration stages subjected to stress corrosion under three conditions

the length of time of these stages are closely related with test environment and concrete type.With the increase of water to binder

the ratio of deterioration was increased

and the length of strength stages was decreased. Immersing drying+30%loading action significantly accelerated the process of stress corrosion damage. Under the action of Immersingdrying +30% load

strengthen section of the length of OPC shorter 67%

compared with the length of time at exposure salt lake. The effect of immersing and drying

HSC Immersingdrying cycles when the stress strength occurred were longer 1.8 times than the OPC and HPC. HSC showed more resistance to stress corrosion in the salt lake regions of china.

关键词

浸烘循环应力腐蚀混凝土相对动弹模量

Keywords

immersing-drying cyclestress corrosionconcreterelative dynamic elastic modulus

references

Views

390

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research on the Energy Dissipation of the Woven Grid Reinforced Concrete

Energy Dissipation of Flexible Fiberand Fiber GridReinforced Concretes

A Loading Device Used for the Test of Concrete Durability

Computational Model of Fly Ash Concrete Compressive Strength Based on the Equivalent Age

The Analysis of Thermal Stress of Concrete Cylinder in the Steady Ax-symmetric Temperature Field

Related Author

LI Weijie

ZHANG Weibiao

HAN Wenbo

HE Junyong

YAO Lining

LI Weijie

HAN Wenbo

ZHANG Weibiao

Related Institution

广东工贸职业技术学院

广东工业大学

．广东工业大学建设学院，广东广州510090，2广东工贸职业技术学院

School of Civil Engineering, Guangzhou University

厦门理工学院土木工程系

Postal code：510275
Tel：020-84112585，84113223 Email：xuebaozr@mail.sysu.edu.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09064830号-19 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰